Pal BGC-2 Grease

PAL BGC-2 GREASE is technologically advanced formula enhanced with ability to absorb vibrations due to high speed. It consists of combination of ester oil, synthetic oil enables higher oxidation stability, excellent corrosion prevention characteristic. A special thickener system offers resistance to steam and mild alkaline and acidic solutions. It also imparts tacky nature improves adhesion which in turns provides superior water resistance property even in chemically wet environment.  It is supplemented with advanced additive system capable of improving wear conditions at high speed also due to strong film formation reduces temperature build up during startups.

---

Product Features

• Ability to absorb vibrations
• Excellent wear resistant characteristic.
• Can operate in wet chemical environment
• Offers superior adhesion, resist water washing off.
• Reduces temperature build up during start up
• Good corrosion and oxidation resistance property.

---

Applications

For high speed plain and threaded spindles in textile. Regular contact bearings, ball bearings in machine tools. Precision gears, electromechanical actuators.

---

Packing

180KG, 18KG, 1KG

---

Characteristics

S.NO.	PROPERTIES	TEST METHOD	PAL BGC-2
1.	Appearance	Visual	Beige
2.	NLGI Grade	DIN 51818	2
3.	Worked Penetration (60 X)	ASTM D 217	265-295
4.	Drop Point, °C, min.	ASTM D 2265	230
5.	Water Wash out, % wt. loss @ 79°C	ASTM D 1264	2.8 (max)
6.	Weld Load, Kg	ASTM D 2596	315
7.	Copper Corrosion 24 hrs. @ 100°C	ASTM D 4048	1b
8.	Base Oil Viscosity @ 40°C, cSt	ASTM D 445	20
9.	SKF EMCOR 1) Distilled water 2) Salt Water	ASTM D6138	0,0 1,1
10.	Speed Factor ndm , mm X min-1, approx.	–	1.2 X 105
11.	Service Temperature range. °C	–	-40 to 160