PAL RUBPRO – A 1000, N 20, P 30
PAL RUBPRO oils are specially developed to improve the processing, mixing operations and reduce compounding time. They modify the physical properties of finished product, minimize power consumption and reduces the cost.
These oils are classified into three groups viz. Aromatics, Paraffinics and Naphthenics.
PAL RUBPRO-A1000 is an aromatic type of oil and is dark in colour. Recommended for use in the manufacturer of automobile tyres, beltings etc. where colour is not an important factor.
PAL RUBPRO-N20 is naphthenic type of oil. It has fairly good colour stability and good high temperature properties. Recommended for use in the manufacture of footwear, mats, moulded and extruded goods.
PAL RUBPRO-P30 is paraffinic type of oil. It is light in colour and has good high temperature properties. Recommended for use in butyl and ethylene propylene rubber for the manufacturer of light coloured rubber goods viz. toys, shoe soles, sports goods and white walled tyres etc.
PRECAUTION
Health: This product is not expected to produce adverse effects on health when used for the intended application. However prolonged or repeated skin contact with this oil is injurious to health. Clean properly with soap and water.
Environment: Lubricant should not be disposed in drain, soil and water. To be disposed through licensed/authorized collector of lubricants only.
PACKING
210 Ltr., Bulk in tankers
CHARACTERISTICS |
Sr.No. |
Properties |
PAL RUBPRO |
| |
|
A 1000 |
N 20 |
P 30 |
1. |
Kin. Viscosity, cSt at 100°C |
22-26 |
----- |
----- |
2. |
Kin. Viscosity, cSt at 40°C |
----- |
20-24 |
30-35 |
3. |
Flash Point, COC, °C, Min |
200 |
160 |
190 |
4. |
Pour Point, °C, Max. |
30 |
-6 |
----- |
5. |
Aniline Point, °C, Min. |
40 |
75 |
90 |
6. |
Molecular Analysis ASTM D 2007 |
|
|
|
|
a) Asphattnes wt.% |
<0.09 |
Nil |
Nil |
|
b) Polar Compounds wt.% |
9.00 |
2.20 |
0.60 |
|
c) Aromatics wt.% |
68.60 |
47.80 |
20.50 |
|
d) Saturates wt. % |
22.40 |
50.00 |
78.90 |